AWS E6010 is a kind of carbon steel electrode with cellulose potassium type coating specially used for vertical downward welding with DC. It has excellent welding performance, beautiful appearance after vertical downward welding, fewer slags and high welding efficiency.
Applications: Suitable for butt welding, fillet welding and lap welding on thin plates, such as low-carbon steel structures like flues of power stations, air ducts, transformer oil tanks, hulls, exterior panels of cars, etc.
X-ray Radiographic Inspection: IIDegree
Instructions:
1. If the electrodes are affected with damp, they must be baked under 80º C for 1.5 hours before welding.
2. The stains on the weldments, such as oil stains, rust, moisture etc., must be cleared away before welding.
3. The electrode weaving should not be too wide and the strength of the arc should be suitable.
Applications: Suitable for butt welding, fillet welding and lap welding on thin plates, such as low-carbon steel structures like flues of power stations, air ducts, transformer oil tanks, hulls, exterior panels of cars, etc.
X-ray Radiographic Inspection: IIDegree
Instructions:
1. If the electrodes are affected with damp, they must be baked under 80º C for 1.5 hours before welding.
2. The stains on the weldments, such as oil stains, rust, moisture etc., must be cleared away before welding.
3. The electrode weaving should not be too wide and the strength of the arc should be suitable.
| Chemical Composition of Deposited Metal (%) | |||||
| Chemical Composition | C | Mn | Si | S | P |
| Guarantee Value | ≤0.20 | 0.30~0.60 | ≤0.30 | ≤0.035 | ≤0.040 |
| General Result | 0.097 | 0.58 | 0.21 | 0.017 | 0.018 |
| Mechanical Properties of Deposited Metal | |||||
| Test Item | Rm(MPa) | ReL(Mpa) | A(%) | AKV(J) | |
| Guarantee Value | ≥420 | ≥330 | ≥22 | ≥27(-30ºC) | |
| General Result | 508 | 406 | 28 | 75 | |
| Reference Current (AC, DC+) | |||||
| Diameter(mm) | φ2.0 | φ2.5 | φ3.2 | φ4.0 | φ5.0 |
| Welding Current (A) | 30~50 | 70~100 | 90~140 | ||